Mae ER70S2 yn wifren MIG a TiG premiwm ar gyfer weldio ar bob gradd o ddur ysgafn a charbon, gan gynhyrchu weldiadau o ansawdd gyda mandylledd lleiaf posibl. Mae'n wifren wedi'i dadocsideiddio driphlyg (Sirconiwm, Titaniwm, ac Alwminiwm) gan ei gwneud yn ddewis ardderchog ar gyfer weldio dros rwd a graddfa felin. Nid oes angen fflwcs gyda'r cynnyrch hwn.
CEISIADAU NODWEDDIADOL:
pibellau a rigiau drilio alltraeth, gwaith dur strwythurol
| Safle Weldio: F, V, OH, H | Cyfredol: DCEP |
| Cryfder Tynnol, kpsi: | 70 |
| Cryfder Cynnyrch, kpsi: | 58 |
| Ymestyniad mewn 2”%: | 22 |
Nodweddiadol o Charpy V-Notch: 35 tr.-lb. Ar -20 gradd F
Cemeg Gwifren Nodweddiadol yn unol ag AWS A5.18 (gwerthoedd sengl yw'r uchafswm)
| C | Mn | Si | P | S | Ni | Cr | Mo | V | Cu | Ti | Zr | Al | ||
| 0.07 | 0.90-1.40 | 0.40-0.70 | 0.025 | 0.035 | 0.15 | 0.15 | 0.15 | 0.03 | 0.50 | 0.05-0.15 | 0.02-0.12 | 0.05-0.15 | ||
| Paramedrau Weldio Nodweddiadol | ||||||||||||||
| Diamedr | Proses | Folt | Amps | Nwy Gwarchod | ||||||||||
| in | (mm) | |||||||||||||
| .035 | (0.9) | GMAW | 28-32 | 165-200 | Trosglwyddo Chwistrell 98% Argon+2% Ocsigen neu 75% Argon+25% CO2 | |||||||||
| .045 | (1.2) | GMAW | 30-34 | 180-220 | Trosglwyddo Chwistrell 98% Argon+2% Ocsigen neu 75% Argon+25% CO2 | |||||||||
| 1/16 | (1.6) | GMAW | 30-34 | 230-260 | Trosglwyddo Chwistrell 98% Argon+2% Ocsigen neu 75% Argon+25% CO2 | |||||||||
| .035 | (0.9) | GMAW | 22-25 | 100-140 | Trosglwyddo Cylched Fer 100% CO2 neu 75% Argon +25% CO2 | |||||||||
| .045 | (1.14) | GMAW | 23-26 | 120-150 | Trosglwyddo Cylched Fer 100% CO2 neu 75% Argon +25% CO | |||||||||
| 1/16 | (1.6) | GMAW | 23-26 | 160-200 | Trosglwyddo Cylched Fer 100% CO2 neu 75% Argon +25% CO | |||||||||
| .035 | (0.9) | GTAW | 13-16 | 60-100 | 100% Argon | |||||||||
| .045 | (1.14) | GTAW | 13-16 | 70-120 | 100% Argon | |||||||||
| 1/16 | (1.6) | GTAW | 12-15 | 100-125 | 100% Argon | |||||||||
| 3/32 | (2.4) | GTAW | 15-20 | 125-175 | 100% Argon | |||||||||
| 1/8 | (3.2) | GTAW | 15-20 | 175-250 | 100% Argon | |||||||||