| Math gradd dur | Dur llwydni: |
| Safonol |
|
| Manylebau cynhyrchu | Plât dur, Taflen, Coil, Bar gwastad, Bar crwn, Dur stribed, gwifren, Pob math o ffugiadau. |
| Peiriannu | Troi Melino Malu Drilio twll dwfn: hyd uchafswm o 9.8 metr. |
| Ystod o waith | Dur bar crwn: 1mm i 2000mm Dur siâp sgwâr: 10mm i 1000mm Plât/dalen ddur: 0.08mm i 800mm Lled: 10mm i 1500mm Hyd: Gallwn gyflenwi unrhyw hyd yn seiliedig ar ofyniad y cwsmer. Gofannu: Siafftiau gyda fflangellau/pibellau/tiwbiau/gwlithod/toesenni/ciwbiau/siapiau eraill Tiwbiau: OD: φ4-410 mm, gyda thrwch wal yn amrywio o 1-35 mm. |
| Triniaeth gwres | Normaleiddio, Anelio, Tymheru, Diffodd, Caledu a thymheru, Sesnin, Caledu arwyneb, Carbureiddio |
CYFANSODDIAD CEMEGOL A PHRIODWEDDAU MECANYDDOL AWS E10015-D2:
| C ≤ | Si ≤ | Mn ≤ | P ≤ | S ≤ | Cr | Ni |
| 0.15 | 0.6 | 1.65-2.0 | 0.03 | 0.03 | ≤0.9 | |
| Mo | Al | Cu | Nb | Ti | V | Ce |
| 0.25-0.45 | ||||||
| N | Co | Pb | B | Arall |
PRIFDDEDDAU MECANYDDOL:
| Priodweddau | Amodau | ||
| T (°C) | Triniaeth | ||
| Dwysedd (×1000 kg/m3) | 7.7-8.03 | 25 |
|
| Cymhareb Poisson | 0.27-0.30 | 25 |
|
| Modwlws Elastig (GPa) | 190-210 | 25 |
|
| Cryfder Tynnol (Mpa) | 1158 | 25 | olew wedi'i ddiffodd, graen mân, wedi'i dymheru ar 425°C |
| Cryfder Cynnyrch (Mpa) | 1034 | ||
| Ymestyn (%) | 15 | ||
| Gostyngiad yn yr Arwynebedd (%) | 53 | ||
| Caledwch (HB) | 335 | 25 | olew wedi'i ddiffodd, graen mân, wedi'i dymheru ar 425°C |
| Priodweddau | Amodau | ||
| T (°C) | Triniaeth | ||
| Dargludedd Thermol (W/mK) | 42.7 | 100 | |
| Gwres Penodol (J/kg-K) | 477 | 50-100 | |
PRIFEDDAU FFISEGOL:
| Nifer | Gwerth | Uned |
| Ehangu thermol | 16 - 17 | e-6/K |
| Dargludedd thermol | 16 - 16 | W/mK |
| Gwres penodol | 500 - 500 | J/kg.K |
| Tymheredd toddi | 1370 - 1400 | °C |
| Tymheredd gwasanaeth | 0 - 500 | °C |
| Dwysedd | 8000 - 8000 | kg/m3 |
| Gwrthiant | 0.7 - 0.7 | Ohm.mm2/m |
Electrodau Weldio Gorchudd Sodiwm Hydrogen Isel E7015-G
DISGRIFIAD:
Mae'n wialen weldio dur tymheredd isel gyda gorchudd sodiwm hydrogen isel sy'n cynnwys nicel. Gellir weldio safle llawn trwy gysylltiad gwrthdro dc. Mewn -80°C mae gan fetel weldio galedwch effaith da o hyd.
DEFNYDDIAU:
Strwythur dur 1.5Ni wedi'i weldio sy'n gweithio -80°C.
CYFANSODDIAD CEMEGOL METAL WEDI'I DYDDODDI:
| C | Mn | Si | Ni | S | P | |
| Safonol | ≤0.08 | ≤1.25 | ≤0.60 | ≥1.00 | ≤0.035 | ≤0.035 |
| Prawf | 0.045 | 0.60 | 0.27 | 1.80 | 0.010 | 0.015 |
PERFFORMIAD MECANYDDOL METAL WEDI'I ADNODDAU:
| Cryfder Tynnol Rm (MPa) | Cryfder Cynnyrch Rel (MPa) | Ymestyniad A (%) | Gwerth Effaith -80°C Akv (J) | |
| Safonol | ≥490 | ≥390 | ≥22 | ≥27 |
| Prawf | 530 | 445 | 30 | 100 |
CERRYN CYFEIRNODOL (DC+):
| Diamedr (mm) | 3.2 | 4.0 | 5.0 | |
| Hyd (mm) | 350 | 400 | 400 | |
| Cerrynt (A) | 90-120 | 140-180 | 180-210 |
| E12015-G | Yn unol â GB E8515-G Yn cyfateb i AWS E12015-G |
Cyflwyniad: Mae E12015-G yn fath o electrod dur cryfder uchel aloi isel gyda gorchudd math sodiwm hydrogen isel. DCRP (Polaredd Gwrthdro Cerrynt Uniongyrchol). Weldio pob safle.
Cymwysiadau: Fe'i defnyddir ar gyfer weldio strwythurau dur cryfder uchel aloi isel gyda chryfder tynnol o tua 830MPa.
Cyfansoddiad Cemegol y Metel a Adneuwyd (%)
| Cyfansoddiad Cemegol | C | Mn | Si | S | P | Mo |
| Gwerth Gwarant | ≤0.15 | ≥1.00 | 0.4~0.8 | ≤0.035 | ≤0.035 | 0.60~1.20 |
| Canlyniad Cyffredinol | ≤0.10 | ~1.50 | ≤0.70 | ≤0.020 | ≤0.020 | ~0.90 |
Priodweddau Mecanyddol Metel a Adneuwyd
| Eitem Prawf | Rm(MPa) | ReL neuRp0.2(Mpa) | A(%) | KV2(J) |
| Gwerth Gwarant | ≥830 | ≥740 | ≥12 | —(tymheredd arferol) |
| Canlyniad Cyffredinol | 860~950 | ≥750 | 12~20 | ≥27 |
Cynnwys Hydrogen Gwasgaradwy mewn Metel Wedi'i Adneuo: ≤5.0ml/100g (Cromatograffeg)
Archwiliad Radiograffig Pelydr-X: Gradd Ⅰ
CYFARWYDDIADAU:
1. Rhaid pobi'r electrodau o dan 350-400 ℃ am awr cyn weldio, eu rhoi mewn can inswleiddio a'u rhoi ar waith cyn gynted ag y bo angen.
2. Rhaid clirio'r staeniau ar y weldiad fel rhwd, a rhaid cynhesu'r weldiad i tua 200 ℃.
3. Gellir tymheru'r weldiad o dan 600-650 ℃ ar ôl weldio er mwyn dileu straen mewnol.